FERUS METALS

FERUS METALS

+359 888 971757

Yavor Y. Stefanov

NONFERUS METALS

NONFERUS METALS

+359 887 428571

Katerinka K. Ilieva

SCRAP CARS

SCRAP CARS

+359 879 222864

Valentin V. Terziysky

OLD OILS

OLD OILS

+359 884 085183

Boris B. Klisursky

EL. APPLIANCES

EL. APPLIANCES

+359 887 428110

Kalina K. Koleva

FERUS METALS

FERUS METALS

+359 888 971757

Yavor Y. Stefanov

NONFERUS METALS

NONFERUS METALS

+359 887 428571

Katerinka K. Ilieva

SCRAP CARS

SCRAP CARS

+359 879 222864

Valentin V. Terziysky

OLD OILS

OLD OILS

+359 884 085183

Boris B. Klisursky

EL. APPLIANCES

EL. APPLIANCES

+359 887 428110

Kalina K. Koleva

Brass and Bronze


DRINK – BRASS FOR PROCESSING

It should consist of min. 61.3% copper, max. 5% iron, brass and bronze turnings, as well as alloyed and contaminated copper scrap. To be exempt from isolated conductors, turnings, electrotype shells and non-metal particles. Hydraulic briquetting of the material is subject to agreement between buyer and seller.

ENERV – TURNINGS FROM RED BRASS
To consist of chips, materials containing red brass and shall be sold on the basis of the sample or analysis.

ELDER – ORIGINAL SUBMERGED BABIN BRASS FERRULE
To consist of bushes and bearings from automobiles and other machinery of red brass, with a babbit high tin at least 12% and should have no bearings with iron base.

ELAND – HARD PARTICLES HIGH CONTENTS OF BRONZE AND LOW CONTENTS OF LEAD
It is recommended that these materials be sold on the basis of the sample or analysis.

ELIAS – HARD BRONZE PARTICLES AND И DRILLING TURNINGS WITH A HIGH CONTENT OF LEAD
It is recommended that these materials be sold on the basis of a sample (test) or analysis..

ENGEL – HARD MACHINE PARTICLES OR HARD BRASS
The contents of copper should not be less than 75%, of tin – not less than 6%, and content of lead – not less than 6% and not more 11%, the total quantity of impurities with the exception of zinc, antimony and nickel not be more than 0, 75%; contents of antimony should not exceed 0.50%. Standard lined and not lined red wagons.

ERIN – MACHINE OR DRILLING TURNINGS WITH BRASS WITH CONTENTS OF COPPER 65-72 % AND 28-35% ZINC
The contents of copper should not be less of 75% and contents of tin – not less than 6%, as the lead contents should not be less than 6% and not more of 11%. The total quantity of impurities with the exception of zinc, antimony and nickel should not exceed 0.75%, and antimony contents should not exceed 0.50%.

FENCE – STANDARD NOT LINED RED WAGONS (clean necks)
To consist of standard not lined and/or separated by melting railway wagons and not lined and/or separated by melting rolling bearing necks of wagons, carriages and no yellow wagons of iron base.

FERRY – STANDARD LINED RED WAGONS (necks)
To consist of standard lined with babbit railway wagons and/or lined with babbit bearing red necks without yellow wagons and wagons of iron base.

GRAPE – CRANES AND VALVES (CAPS)
Consist of mixed clean red or yellow brass, including chromium and nickel-plated without cranes for gas, beer and material for castings of aluminum and zinc base, and the minimum content of half-red in them is 35%.

HONEY – YELLOW BRASS SCRAP
It consists of brass castings, rolled brass, reinforced brass, pipes and other yellow brass parts, including brass coated particles. To be without manganese bronze, aluminum bronze, without radiators or radiator parts, without iron too unclean or materials with corrosion.

IVORY – YELLOW BRASS CASTINGS
Consist of yellow brass castings with crucible form, none of the pieces is longer than the others by more than 12 inches; without brass forgings, silicon bronze, do not contain nickel-plated material of over 15%.

LABEL – НОВИ МЕСИНГОВИ ИЗРЕЗКИ
Consist of clippings from new unleaded leaves or yellow brass plates, are free of impurities and not containing more than 10% pure brass trimmings into ј inches. To have no metal-munts and marine brass.

LACE – BRASS WALL CASING WITHOUT PRIMER
Contain heat cleaned 70/30 brass walls of casings with brass primer and without impurities from other materials.

LAKE – SMALL BRASS GRIPS AND LINING OF A FIREARM, THERMAL CLEANED
Consist of thermal cleaned 70/30 brass linings, without bullets, iron or other materials.

LAMB – SMALL BRASS GRIPS AND LININGS OF FIREARM, MUFFLE CLEANED (SECONDARY CRUMBLED)
Consist of muffle cleaned (secondary crumbled) 70/30 brass linings, without bullets, iron and other materials.

LARK – YELLOW BRASS PRIMER
Of yellow brass primer, burned or not. Without iron, are not overly polluted, no corrosion on them and without other materials.

MAIZE – NEW MIXED NICKEL BRONZE CLIPPINGS
Consist of one or more brass alloy, with a specified content of nickel, without chrome or other coating material. Brass clippings with lead coating should be packed and sold separately. Do not contain more than 10% pure clippings of less than ¼ inches.

MAJOR – NEW CLIPPINGS AND HARD PARTICLES OF NICKEL BRONZE (BRASS)
To contain new and clean brass clippings, plates, rods and forgings as well as other rolled shapes, to be without chromium or other tiling. Be sold on the basis of specified content of nickel, as 10-12%-15%-18%-20%. Lined with lead brass clippings to be packaged and sold separately. When offering any kind of brass material the physical characteristics should be indicated.

MALAR – NEW SORTED BY SIZE (SEGREGATED) CLIPPINGS OF NICKEL BRONZE
To consist of a particular type of Brass alloy. Do not contain more than 10% pure clippings of ¼ inches.

MALIC – OLD NICKEL BRONZE
Consist of cemented or not sheets, bars, tubes, wire, bars with nickel bronze. Should not be with separately cleaned joints and is free of impurities, without iron plating material and other metals.

MELON – BRASS PIPES
Consist of brass pipes without coating and sealed materials or pipes with shed brass joints. Pipes should be strong, clean, without sludge or condenser tubes.

NAGGY – NICKEL BRONZE MOULDING
To be packed and sold separately.

NIECE – NICKEL BRONZE TURNINGS
Sold on the basis of sample or analysis.

NIGHT – TURNINGS OF YELLOW BRASS BARS
Consist of turnings of bars only, without aluminum contents, manganese, no turnings of Tobin, muntz metal, traces of moisture or other moisture; to be without flakes and antifriction; to contain not more than 0.30% tin and not more of 0.15% alloy steel.

NOBLE – NEW YELLOW BRASS ROD ENDS
To consist new, clean rod ends, without free turning brass or forging rods, not to consist more than 0.30% tin and not more than 0.15% alloy steel. No muntz metal or sea brass, or other composite materials. Pieces are not larger than 12 inches without impurities.

NOMAD – YELLOW BRASS TURNINGS
Consists of yellow brass chips without aluminum, manganese and combined chips; do not consist free iron above 3%, fats or other moisture; without small particles and Babbitt. To prevent disputes, material to be sold based on sample or analysis.

OCEAN – MIXED UNSEPARATED WITH SOLDER CAR RADIATORS
Consist of mixed automobile radiators without aluminum and iron-ribbed radiators. For all radiators with iron a discount is granted. Tonnage specification should cover the gross weight of the radiators, unless otherwise is indicated.

PALES – CONDENSER PIPES OF ADMIRAL BRASS
To consist of strong paneled or not condenser pipes of admiral brass. To be clean of nickel and aluminum alloy, no corrosion material.

PALLU – CONDENSER PIPES OF ALUMINUM BRASS
To consist of clean, strong paneled or not condenser pipes. To be clean of nickel and aluminum alloy, no corrosion material.

PALMS – MUNTZ METAL PIPES
To consist of clean, strong paneled or not muntz metal pipes. To be clean of nickel and aluminum alloy, no corrosion material.

PARCH – HARD PARTICLES BRASS BRONZE
Copper contents should not be less than 55%, and the lead contents should not be more than 1%, without aluminum bronze and silicone bronze.